文章信息/Info

Title:

Research Progress on the Corrosion Behavior of Aluminum Alloys under Marine Environment

文章編號:

1674-3962(2022)06-0477-10

作者:

呂曉丹; 劉斌; 劉巖; 劉蔚; 田華陽

（北京化工大學材料科學與工程學院 材料電化學過程與技術北京市重點實驗室，北京 100029）

Author(s):

LV Xiaodan;  LIU Bin;  LIU Yan;  LIU Yu;  TIAN Huayang

(Beijing Key Laboratory of Materials Electrochemical Process and Technology, College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China)

關鍵詞:

鋁合金; 海洋環(huán)境; 腐蝕行為; 實驗方法; 表征方法

Keywords:

aluminum alloy;  marine environment;  corrosion behavior;  experimental methods;  characterization methods

分類號:

TG172.5

DOI:

10.7502/j.issn.1674-3962.202005042

文獻標志碼:

A

摘要:

近年來，隨著世界各國對海洋資源開發(fā)與利用的不斷重視，航海裝備得到了快速發(fā)展，對裝備輕量化的需求也日益突顯。鋁合金因其密度小、比強度高，作為結(jié)構(gòu)材料使用可以大幅度提高航海裝備的運載能力和速度，而被廣泛應用。但是，在海洋腐蝕環(huán)境作用下，鋁合金易受到多種類型腐蝕的破壞，表現(xiàn)出極為特殊的腐蝕行為規(guī)律，嚴重影響其使用�；�于國內(nèi)外相關研究現(xiàn)狀，對鋁合金在不同海洋環(huán)境條件下的腐蝕類型、腐蝕行為規(guī)律、試驗與研究方法等進行了綜合分析，總結(jié)了存在問題，針對性地提出了解決方法和技術途徑，并對此研究領域未來的發(fā)展前景進行了展望。

Abstract:

In recent years, with the increasing attention on the development and utilization of marine resources worldwide, marine equipments have been developed rapidly, and the requirements for lightweight equipment become more and more urgent. Attributed to its low density and high specific strength, aluminum alloys are widely used as structural materials to improve the carrying capacity and speed of marine equipments. However, under marine corrosive environment, aluminum alloys are susceptible to various types of corrosion, which will seriously affect its application, and aluminum alloys exhibit very special corrosion behavior. Based on the current research status, the corrosion types, the corrosion behavior, test and research methods of aluminum alloys under different marine environments were analyzed comprehensively in this article. At the same time, the existing problems were summarized, while corresponding solutions and technical approaches were also put forward. Finally, the future development prospect of this research field was proposed.