Self-Healing Polyoxime-Urethane Elastomers Based on Multiple Dynamic Bonds

文章編號(hào):

1674-3962(2025)09-0874-07

作者:

金宇慧; 薛振華; 吳澤凱; 陳海龍; 晏雪生; 游正偉

1. 東華大學(xué)材料科學(xué)與工程學(xué)院 纖維材料改性國(guó)家重點(diǎn)實(shí)驗(yàn)室, 上海 201600 2. 浙江禾欣科技有限公司，浙江 嘉興 314000

Author(s):

JIN Yuhui; XUE Zhenhua; WU Zekai; CHEN Hailong; YAN Xuesheng; YOU Zhengwei

1. State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Science and Engineering, Donghua University, Shanghai 201600, China 2. Zhejiang Hexin Science and Technology Co., Ltd., Jiaxing 314000, China

關(guān)鍵詞:

聚氨酯; 金屬配位; 多重動(dòng)態(tài)鍵; 自愈合; 對(duì)苯醌二肟

Keywords:

polyurethane;  metal coordination;  multiple dynamic bonds;  self-healing;  p-benzoquinone dioxime

分類號(hào):

O631.5

DOI:

10.7502/j.issn.1674-3962.202404004

文獻(xiàn)標(biāo)志碼:

A

摘要:

利用兩步法將對(duì)苯醌二肟（BQDO）、聚四氫呋喃二醇（PTMG）和異佛爾酮二異氰酸酯（IPDI）反應(yīng)合成得到含有動(dòng)態(tài)肟氨酯鍵（BQDU）的自愈合聚氨酯彈性體（BQDU-LPU）。進(jìn)一步引入銅離子構(gòu)筑了一系列具有氫鍵、肟氨酯鍵和金屬配位鍵多重動(dòng)態(tài)鍵的聚肟氨酯彈性體（Cu-BQDU-LPUs）。通過(guò)核磁共振氫譜儀和傅里葉變換紅外光譜儀對(duì)彈性體的結(jié)構(gòu)進(jìn)行表征，并采用熱重分析儀、動(dòng)態(tài)熱機(jī)械分析儀和電子萬(wàn)能材料試驗(yàn)機(jī)測(cè)試彈性體的熱學(xué)性能、力學(xué)性能和愈合性能，系統(tǒng)研究了銅離子的引入對(duì)彈性體性能的影響規(guī)律。結(jié)果表明，銅離子的引入能同步提升彈性體的熱穩(wěn)定性與力學(xué)性能。在制備的一系列Cu-BQDU-LPUs（2.5% Cu-BQDU�睱PU、5% Cu-BQDU-LPU、7.5% Cu-BQDU-LPU和10%Cu-BQDU-LPU）中，5% Cu-BQDU-LPU具有最佳的力學(xué)性能（拉伸強(qiáng)度為（15.8±2.7）MPa，韌性為（92.7±31.5）MJ/m3，楊氏模量為（5.0±0.4）MPa）；在70 ℃下加熱2 h愈合效率可達(dá)（90.9±2.9）%。

Abstract:

In this study, we employed a two-step approach to synthesize self-healing polyurethane elastomers (BQDU-LPU) containing dynamic oxime-urethane bonds (BQDU) by reacting p-benzoquinone dioxime (BQDO),polytetramethylene ether glycol (PTMG) and isophorone diisocyanate (IPDI). Subsequently, a series of Cu-BQDU-LPUs elastomers possessing triple dynamic bonds, including hydrogen bonds, oxime-amide bonds and metal coordination bonds were constructed by introducing copper ions. The structure of elastomers was characterized by nuclear magnetic resonance spectroscopy and Fourier-transform infrared spectroscopy, while their thermal, mechanical and self-healing properties were evaluated using thermogravimetric analysis,dynamic mechanical analysis and electronic universal material testing machine, respectively. The influence of copper ions on the properties of elastomers was systematically investigated. The results demonstrated that the introduction of copper ions simultaneously enhance the thermal stability and mechanical properties of the elastomers. Among the series of Cu-BQDU-LPUs,the 5% Cu-BQDU-LPU exhibited optimal mechanical properties,characterized by a tensile strength of (15.8±2.7) MPa, toughness of (92.7±31.5) MJ/m3 and Young’s modulus of (5.0±0.4) MPa. When subjected to heating at 70 ℃ for 2 h, this particular composition displayed a healing efficiency up to (90.9±2.9)%.